粉煤灰综合利用 2017 NO.3FLYASHCOMPREHENSIVEUTILIZATION 试验与应用
复合改性低品质粉煤灰在混凝土中的应用研究 Research on Application of the Composite Modified Low Quality of Fly Ash in Concrete
周美茹，陈国强，李军锁 （河北建材职业技术学院，秦皇岛066004） 摘要：针对低品质粉煤灰存在的水化活性低、流动性差等问题，在粉磨改性的基础上采用粉磨+流化床气相沉 积的处理方法，对低品质粉煤灰进行复合改性，在减水剂用量相同时，复合改性粉煤灰表现出明显的减水效果，采用 复合改性的低品质粉煤灰制备的混凝土，工作性得到明显改善，28d龄期强度提高一个强度等级，每立方混凝土可节 约成本5~6元，对充分利用劣质粉煤灰具有实际指导作用。
关键词：粉煤灰复合改性混凝土 中图分类号：TU528.2文献标识码：A文章编号：1005-8249（2017）03-0016-03 Zhou Meiru, Chen Guoqiang, Li Junsuo (Hebei Construction Meterial Vocational and Technical College, Hebei Qinhuangdao, 066004 ) p ou b d pupq qnenboqj sqdoau sq grinding+fluidized bed vapor deposition）was put forward to modify fly ash. The posite modified fly ash can exhibit more effeet of water reducing than unmodified fly ash, on the condition of equal adition of water reducer. The conerete that was made from modified fly ash has ramatically improved the work ability, and its strength at 28d age increased ne strength gade. It can save costs of 5 to 6 yuan percubicmetr f concrete it played a pactical guiding role to the lowquality fly ash. Keywords: fly ash; posite modification; concrete 早在20世纪50年代粉煤灰就已在混凝土中广的经济、环保及节能等综合效益，显得非常重要。
泛应用1，由于粉煤灰能大大改善混凝土的工作性、1低品质粉煤灰的复合改性试验 力学性能、抗裂抗渗性能及耐久性能，在建材工业、 建筑工程、筑路工程的混凝土中利用的粉煤灰约占1.1试验用原材料 粉煤灰综合利用的90%（3，粉煤灰在混凝土中的应试验用原材料包括：秦皇岛热电厂干排原状粉 用已经成为粉煤灰高附加值利用的主要途径。
国标煤灰；水泥为秦皇岛浅野水泥有限公司产PⅡ42.5 将粉煤灰分为I、Ⅱ、Ⅲ级，低品质粉煤灰，即Ⅲ硅酸盐水泥；改性材料采用NaSO.（NS）和表面活 级及等外灰。
在原状灰中，I级粉煤灰仅占排灰量性剂按照质量比1：3配制而成；标准砂和自来水。
的5%，随着应用技术的研究和工程应用的推广，参照国家标准《GB/T1596-2005用于水泥和混凝土中 优质粉煤灰已经出现严重短缺。
由于低质粉煤灰的粉煤灰》，对秦皇岛电厂干排原灰的细度、需水量比 需水量比高，烧失量大，活性指数低，与外加剂的及活性指数等进行基本性能测试，原状灰的基本性 适应性差等缺点，在应用过程中受到了一定的限制，能参数见表1。
在混凝土中利用好低品质粉煤灰，真正发挥粉煤灰表1粉煤灰基本性质参数原料名称/% 45μm筛余需水量比3d活性指数28d活性指数 *基金项目：河北省重点科技项目（16273805D）811541.5858.65 第一作者：周美茹（1968-）教授，Email:1069080830@qq.由表1可知，原状粉煤灰的颗粒较粗，需水量 通讯作者：李军锁（1962-）教授，Email:@163.比较大，活性指数较低，参照标准属于等外灰。
收稿日期：2017-04-11 16 万方数据
粉煤灰综合利用 FLYASHCOMPREHENSIVEUTILIZATION2017 NO.3
试验与应用 1.2复合改性方法（4）试验。
首先，接通空压机电源，使其储存 复合改性是物理...