粉煤灰综合利用 2016 NO.2FLYASHCOMPREHENSIVEUTILIZATION 试验与应用
改性粉煤灰吸附处理含铜废水的试验研究
高玉红，魏蕊娣，任立伟
（邯郸学院化学化工与材料学院，河北邯郸056005） 摘要：分别用碱、酸、高温、超声波和助溶剂对粉煤灰进行改性，对每种改性粉煤灰吸附处理含铜废水进行研究。
试验结果表明：其中碱、高温、助熔剂都可改性粉煤灰，碳酸钠助熔剂改性效果最好，其最佳反应时间是30min，最适宜反 应温度是20℃，最适宜pH值是10。
吸附过程符合Temkin和Langmuir吸附等温式。
关键词：改性粉煤灰；含铜废水；吸附 中图分类号：X773文献标识码：A文章编号：1005-8249(2016)02-0018-04
Gao Yuhong, Wei Ruidi, Ren Liwei (School of Chemical and Materials, HanDan College, HanDan) Abstract: Fly ash was modified by Sdium hydroxide, Sulfuric acid, high temperature, ultrasonic and Sodium cabonate co=solvent. It' s investigated adsorption characteristics and the optimal adsorption coditons of Coppercontaining wastewater by modified ly ash. Results show that y ash canbe mdiied by the sdium hyroxide,high temperatre an solvent. dim arbate csolvent s thebest. he experimetal reuls show that: the optimum reaction time is 30 minutes, the most appropriate reaction temperature is 20 °C, the optimum pH value is 10. The adsorption processof Copper-cntaining wastewater on alkalimodified fly ash accords with Temkin and langmuir isotherm equations. Key Words:Modified fly ash; Copper=containing wastewater; Adsorption 粉煤灰是燃煤电厂煤燃烧后的灰，简称飞灰进行改性，吸附处理模拟含铜废水，筛选出了最有效的 (fly ash）。
2013年我国粉煤灰的年产量约为5.32改性方法，为改性粉煤灰在污水处理领域的进一步应 亿t,粉煤灰会对空气、土壤和淡水造成污染。
在环用提供参考。
保方面，粉煤灰具有较大的比表面积，拥有很多Al、Si 的活性点，使粉煤灰可以像活性炭一样具有很好的吸1试验 附能力，吸附后的粉煤灰不需要再生，可以直接用于生1.1材料和仪器 产水泥等，充分利用了资源。
在冶金和电镀等生产过模拟废水：用三水合硝酸铜配置49.5mg/L的含铜 程中会产生大量的含铜废水，化学混凝沉淀法、离子交模拟废液。
换法、电解法、反渗透法和电渗析法等是目前工业上处吸附剂：粉煤灰，取自邯郸市某发电厂，品质为1 理含铜废水的主要方法3。
未经改性的粉煤灰吸附级灰，其成分主要有SiO2、AlO,、FeO、CaO和未燃尽 能力不高，若将粉煤灰更好的应用于污水处理就必须的碳，还有少量的MgO、Na20和K20等。
进行改性处理，本文采用了5种不同的方法对粉煤灰主要仪器：TAS-986火焰原子吸收仪，KQ-250DB “基金项目：河北省教育厅高等学校科学技术研究项目，项目编数字超声波清洗仪，DRZ-4马弗炉，FA2004B电子天 号：Z2015040平，152型电热恒温干燥箱，SHA-B恒温振荡器，PHS 第一作者：高玉红（1976～），女，汉族，副教授，硕士，现从事污水处-3CpH计等。
理与控制的研究与教学工作。
1.2粉煤灰的改性 Email ;hdgaoyuhong@ 126.主要包括NaOH改性；硫酸改性；超声改性；高温 收稿日期：206-10-14 18
万方数据
粉煤灰综合利用 FLYASHCOMPREHENSIVEUTILIZATION2016 NO.2
试验与应用 焙烧改性和无水碳酸钠作为助溶剂的改性，改性过程80 参考作者发表论文[-]。...