施工技术2013年5月上 96CONSTRUCTIONTECHNOLOGY第42卷第9期 DOI:10. 7672/sgjs2013090096
秸秆粉末保温页岩烧结砖性能研究
扈峥，李冰，欧阳金龙 （四川大学建筑与环境学院，四川成都610065）
[摘要】试验以页岩烧结砖的原料组分及物理特性为基础，以农业秸秆废料作为添加剂，按照一定的配合比和成型 工艺，研制开发节能保温页岩烧结砌块。
在试验过程中对孔隙率和抗压强度等多项指标进行测试，结果表明：样本 各项性能均能达到《烧结普通砖》GB5101一2003相关要求。
并进一步探讨了秸秆粉末的含量对砌块孔隙率、抗压 强度等特性的影响，为后续试验的开展和深人研究提供了基础数据支持。
[关键词]保温；秸秆；烧结页岩砌块；材料试验 [中图分类号]TU522[文献标识码]A[文章编号]1002-8498（2013)09-0096-03 ResearchonPerformanceofStrawPowder InsulationShaleSinteredBrick Hu Zheng, Li Bing， Ouyang Jinlong (Architecture and Environment College of Sichuan University，Chengdu，Sichuan 610065，China) Abstract;Based on the raw material position and physical characteristics of shale sintered bricks， and using agricultural straw waste as an additive, tests were designed according to certain mix proportion and molding process to develop thermal-insulation and energy-saving shale sintered bricks.Parameters such as porosity and pressive strength were measured during the tests. The result shows that all brick samples could satisfy the requirements of the standard for sintered bricks. The influence of the ratio of the straw powder on the blocks’ characteristics such as porosity and pressive strength was discussed. This work provided basic data support for subsequent and in - depth research. Key words;insulation; straw; sintered shale brick;materials test
0引言表1页岩级配 本文提出一种新型砌体材料，以页岩为主要原Table 1 Shale particle size gradation 料，通过在泥料中添加一定细度的秸秆粉末，经过200>50~000-01-501</ 压力成型和烧结等步骤，形成一种轻质微孔页岩砌所占比例/%601010812 体材料。
1.1.2秸秆选用 1试验方法试验选用粉碎后的秸秆粉末作为有机成孔剂。
1.1材料选用材料取自成都市周边水稻、玉米等农作物的秸秆废 1.1.1页岩选用弃物，通过机械粉碎后放置于室内环境下自然干 本试验中所使用页岩原料取自成都市双流县，燥。
为确保秸秆粉末粒径能够满足试验要求，故抽 为确保页岩颗粒符合试验制砖要求，使用前已经过取1kg秸秆粉末用标准筛进行筛分测试。
秸秆粉末 砖厂设备进行粉碎。
泥料制备前，用标准筛对页岩直径分布如表2所示。
粉末颗粒级配进行筛分，页岩颗粒级配如表1所示。
表2秸秆粉末颗粒级配 经过筛分测试，试验所采用的页岩具有合理的Table 2Straw powder particle size gradation 颗粒级配，能够满足普通页岩烧结砖的基本要求。
直径/mm21~2 0.5~10.25~0.5 0.075~0.25<0.075 质量/g336632921271 所占比例/%0.30.133.533.521.67.2 [作者简介]患静，硕士研究生，E-mail：trapan@ [收稿日期]2013-01-22经过筛分，秸秆...